Deposition of Steel over Steel by Friction Surfacing Technique and Investigation of its Physical Geometry
Friction surfacing (FS) is a coating technique inspired by friction stir welding. FS is a solid-state, thermo-mechanical process providing excellent wear and corrosion resistance properties. Frictional heating elevates the temperature of the consumable rotating tool (m...
Đã lưu trong:
| Những tác giả chính: | , , , , |
|---|---|
| Định dạng: | Bài viết |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
Research and Development Wing, MIST
2025
|
| Những chủ đề: | |
| Truy cập trực tuyến: | http://dspace.mist.ac.bd:8080/xmlui/handle/123456789/887 |
| Các nhãn: |
Không có thẻ, Là người đầu tiên thẻ bản ghi này!
|
| Tóm tắt: | Friction surfacing (FS) is a coating technique inspired by friction stir welding. FS is a solid-state, thermo-mechanical process providing excellent wear and corrosion resistance properties. Frictional heating elevates the temperature of the consumable rotating tool (mechtrode) up to the softening of the material, the tool is traversed along the length of the plate, and the material gets deposited onto the substrate plate with good mechanical properties and excellent corrosion resistance properties, FS process may have wider application in the mining industry to provide an adequate coating on excavator's teeth, shovel teeth, and dragline teeth. This paper has an experimental approach to investigate the coating integrity during the FSed deposition of AISI4140 (consumable rod) over EN24 plate on a conventional milling machine. Various testslike wear test, XRD analysis, hardness, IR thermography, surface roughness, FESEM images have been analysed. Experiments have shown that at a low travel speed of 16mm/min, the coating is non-uniform and an excessive increase in travel speed will not give proper time for softening of the material, resulting in a discontinuous coating so the optimum travel speed must be chosen for better quality coating. Also, one more approach has been made to explore the effect of mechtrode shapes on the flash formation of the consumable tool while deposition of mild steel over mild steel on the milling machine where conical cylinder tool shape wasmore efficiently worked. |
|---|