Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments
The current study was conducted to compare the wear behaviour and frictional nature of three commonly used commercial polymers namely, uPVC (Unplasticized polyvinyl chloride), High Density Polyethylene (HDPE) and Acrylic. The aim was to find out the effect of various loads at various sliding dist...
Shranjeno v:
| Main Authors: | , , |
|---|---|
| Format: | Thesis |
| Jezik: | angleščina |
| Izdano: |
DEPARTMENT OF MECHANICAL ENGINEERING
2021
|
| Online dostop: | http://dspace.mist.ac.bd:8080/xmlui/handle/123456789/655 |
| Oznake: |
Brez oznak, prvi označite!
|
| _version_ | 1868226984532770816 |
|---|---|
| author | Labonee, Monzila Farzana Rahman, Mohammed Sajidur Fazlullah, Fahim |
| author_browse | Fazlullah, Fahim Labonee, Monzila Farzana Rahman, Mohammed Sajidur |
| author_facet | Labonee, Monzila Farzana Rahman, Mohammed Sajidur Fazlullah, Fahim |
| author_sort | Labonee, Monzila Farzana |
| collection | DSpace |
| description | The current study was conducted to compare the wear behaviour and frictional nature of
three commonly used commercial polymers namely, uPVC (Unplasticized polyvinyl
chloride), High Density Polyethylene (HDPE) and Acrylic. The aim was to find out the
effect of various loads at various sliding distances on wear characteristics and frictional
nature of the materials. A vertical pin-on-disk method was used throughout the
experiment. All experiments were carried out in normal ambient conditions of relatively
high summer temperatures (approximately 30⁰C) and high relative humidity (80%). The
sliding velocity was kept at 0.6397 m/s and the sliding distance was varied from 192.423
m to 4618.152 m. The loads were 0.025 kg, 0.5 kg, 1.0 kg, and 2.0 kg respectively. The
experiments were done in three different surface mating conditions, dry, wet and claywater. It was verified that the weight loss increased with increase in sliding distance and
load. Density and hardness of the different polymers were also measured. Also it was
studied to see whether the wear behaviour and frictional resistance had any correlation to
each other and it was found that there was no noticeable relationship between wear rate
and friction coefficient (µ). However both the frictional coefficient and wear rate varied
with load. Different surface mating conditions (dry, wet and clay-water) showed effect on
the friction coefficient (µ) and wear rate as well. It was found that in general friction
coefficient (µ) of HDPE was least of the three in all experimental conditions, while acrylic
had the highest, and uPVC fell in between. The wear behaviour also showed a similar
trend in that HDPE had the least wear for a given load at a particular sliding distance and
at a specified surface mating condition while Acrylic showed the most wear with uPVC
falling in between. The reason behind the excellent wear and frictional behaviour of
HDPE is due to the difference in the crystallinity of the three polymers. HDPE is almost
fully crystalline in nature while Acrylic is almost fully amorphous and uPVC has higher
portions of crystalline region compared to acrylic. Generally the higher the crystallinity
the better the frictional and wear characteristics of any material. Optical microscopic
analysis of the specimen, dust and disk was also made. EDX and ESM observations were
also made which showed that uPVC was most affected by oxidation followed by HDPE
and then Acrylic. |
| format | Thesis |
| id | oai:localhost:123456789-655 |
| institution | My University |
| language | English |
| publishDate | 2021 |
| publishDateRange | 2021 |
| publishDateSort | 2021 |
| publisher | DEPARTMENT OF MECHANICAL ENGINEERING |
| publisherStr | DEPARTMENT OF MECHANICAL ENGINEERING |
| record_format | dspace |
| spelling | oai:localhost:123456789-6552021-10-04T06:42:39Z Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments Labonee, Monzila Farzana Rahman, Mohammed Sajidur Fazlullah, Fahim The current study was conducted to compare the wear behaviour and frictional nature of three commonly used commercial polymers namely, uPVC (Unplasticized polyvinyl chloride), High Density Polyethylene (HDPE) and Acrylic. The aim was to find out the effect of various loads at various sliding distances on wear characteristics and frictional nature of the materials. A vertical pin-on-disk method was used throughout the experiment. All experiments were carried out in normal ambient conditions of relatively high summer temperatures (approximately 30⁰C) and high relative humidity (80%). The sliding velocity was kept at 0.6397 m/s and the sliding distance was varied from 192.423 m to 4618.152 m. The loads were 0.025 kg, 0.5 kg, 1.0 kg, and 2.0 kg respectively. The experiments were done in three different surface mating conditions, dry, wet and claywater. It was verified that the weight loss increased with increase in sliding distance and load. Density and hardness of the different polymers were also measured. Also it was studied to see whether the wear behaviour and frictional resistance had any correlation to each other and it was found that there was no noticeable relationship between wear rate and friction coefficient (µ). However both the frictional coefficient and wear rate varied with load. Different surface mating conditions (dry, wet and clay-water) showed effect on the friction coefficient (µ) and wear rate as well. It was found that in general friction coefficient (µ) of HDPE was least of the three in all experimental conditions, while acrylic had the highest, and uPVC fell in between. The wear behaviour also showed a similar trend in that HDPE had the least wear for a given load at a particular sliding distance and at a specified surface mating condition while Acrylic showed the most wear with uPVC falling in between. The reason behind the excellent wear and frictional behaviour of HDPE is due to the difference in the crystallinity of the three polymers. HDPE is almost fully crystalline in nature while Acrylic is almost fully amorphous and uPVC has higher portions of crystalline region compared to acrylic. Generally the higher the crystallinity the better the frictional and wear characteristics of any material. Optical microscopic analysis of the specimen, dust and disk was also made. EDX and ESM observations were also made which showed that uPVC was most affected by oxidation followed by HDPE and then Acrylic. 2021-10-04T06:42:36Z 2021-10-04T06:42:36Z 2017-12 Thesis http://dspace.mist.ac.bd:8080/xmlui/handle/123456789/655 en application/pdf DEPARTMENT OF MECHANICAL ENGINEERING |
| spellingShingle | Labonee, Monzila Farzana Rahman, Mohammed Sajidur Fazlullah, Fahim Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title | Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title_full | Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title_fullStr | Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title_full_unstemmed | Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title_short | Comparative Analysis of Wear Behaviour of Commercial Polymeric Pipe Materials under Different Sliding Environments |
| title_sort | comparative analysis of wear behaviour of commercial polymeric pipe materials under different sliding environments |
| url | http://dspace.mist.ac.bd:8080/xmlui/handle/123456789/655 |
| work_keys_str_mv | AT laboneemonzilafarzana comparativeanalysisofwearbehaviourofcommercialpolymericpipematerialsunderdifferentslidingenvironments AT rahmanmohammedsajidur comparativeanalysisofwearbehaviourofcommercialpolymericpipematerialsunderdifferentslidingenvironments AT fazlullahfahim comparativeanalysisofwearbehaviourofcommercialpolymericpipematerialsunderdifferentslidingenvironments |